Polyaspartic Polyurea Flooring Midcoat
Performance Features: High elongation, high tensile strength, high elasticity, and excellent wear resistance. Widely used for roof waterproofing and elastic flooring midcoat.
Your Trusted Supplier Of Polyaspartic Resin
Polyaspartic polyurea material is an innovative aliphatic, slow-reacting, high-performance coating in the polyurea industry, known as the third generation of polyurea.
MPU specializes in polyaspartic resins, amine compounds, and latent curing technology. After years of product development, we have launched a cost-effective series of polyaspartic resins and amine compounds to meet various application needs. Our products are widely used in wind power anti-corrosion, engineering waterproofing, building flooring and exterior walls, furniture, and the automotive industry.
We offer OEM/ODM services, customizing packaging to match your brand colors. With our chemical expertise, we are confident in delivering solutions that exceed your expectations.
Definition of Polyaspartic Resin
Polyaspartic resin is a yellowing-resistant, slow-reacting, high-performance material widely used in pipeline anti-corrosion, tunnel waterproofing, bridge protection, industrial coatings, roofing waterproofing, polyurea sealants, exterior wall coatings, and industrial flooring.
Polyaspartic Resin And Curing Agent
| Polyaspartic resin | |||||||
|---|---|---|---|---|---|---|---|
| Resin Model | Relative Density (25℃) | Viscosity mpa.s (25℃) | Solid Content % | Equivalent Weight | Hydroxyl Content % | Gel Time min | Characteristics |
| 1420 | 1.06 | 800 - 1200 | 99±1 | 277 | 6.14 | 18 | Medium - viscosity, fast - curing, for coatings |
| 1520 | 1.06 | 800 - 1200 | 99±1 | 291 | 5.84 | 100 | Medium - viscosity, slow - curing, for manual polyurea |
| 1524 | 1.06 | 1500 - 1800 | 99±1 | 333 | 5.10 | 26 | Medium - viscosity, moderate - speed, for manual polyurea |
| 1472 | 1.07 | 300 - 500 | 99±1 | 236 | 7.20 | 5 | Low - viscosity, fast - gelling, suitable for spraying |
| 1230 | 1.05 | 300 - 500 | 99±1 | 287 | 5.92 | 30 | Low - viscosity, fast - gelling, suitable for spraying |
| 1490 | 1.07 | 300 - 500 | 99±1 | 243 | 7.00 | 2 | Low - viscosity, fast - curing, for rock slab adhesive |
| 5208 | 1.05 | 800 - 1200 | 99±1 | 299 | 5.69 | 100 | Medium - viscosity, slow - curing, for manual polyurea |
| 4560 | 1.04 | 900 - 1300 | 99±1 | 347 | 4.90 | 120 | Medium - viscosity, slow - curing, for manual polyurea |
| 4250 | 1.05 | 600 - 1000 | 99±1 | 236 | 7.2 | 20 | Medium - viscosity, moderate - speed, for waterproofing and protection |
| 2231 | 1.06 | 700 - 1000 | 99±1 | 250 | 6.8 | 20 | Resin for tile joint sealant |
| 5516 | 1.0 | 1500 - 2000 | 99±1 | 1839 | 0.92 | 30 | Low - hardness, high - equivalent - weight, elastic coating |
| Curing agent | ||||
|---|---|---|---|---|
| Curing Agent Model | NCO% | Viscosity mpa.s (25℃) | Solid Content % | Characteristics |
| H - 100 | 21.0 - 21.5 | 1000 - 1500 | 100 | Low - cost, colorless and transparent |
| H - 300 | 19.5 - 20.5 | 200 - 700 | 100 | Low - viscosity, colorless and transparent |
| H - 600 | 22.0 - 23.0 | 500 - 1000 | 100 | Low - viscosity, high - cost |
| H - 1010 | 9.5 - 10.0 | 300 - 800 | 100 | Elastic curing agent |
| H - 442 | 14.0 - 14.5 | 1000 - 1500 | 100 | Low - viscosity, for floor and tile joint |
| H - 333 | 14.0 - 14.5 | 1000 - 1500 | 100 | Low - cost, no free monomer |
| H - 3004 | 14.0 - 14.5 | 700 - 1000 | 100 | Low - viscosity, good low - temperature resistance, for tile joint and spraying |
| H - 9100 | 22.5 - 23.0 | 1500 - 2000 | 100 | Extremely low - cost, dark - colored and transparent, for dark - colored coatings |
Application of Polyaspartic Resin
Polyaspartic Resin waterproof coating
Building facade and swimming pool water park
- Excellent weather resistance
- Crack-resistant, fully encapsulated, prevents tile detachment
- Anti-corrosion and anti-mildew, scrub-resistant, stain-resistant
- Eco-friendly and highly safe to use
Polyaspartic polyurea elastic waterproof coating for dams and tunnels
- Performance features: High elongation, high tensile strength, high elasticity, and high wear resistance
Polyaspartic polyurea anti-corrosion coating
Using advanced technology, this coating is formulated with high-performance aliphatic polyaspartic polyurea resin and aliphatic isocyanate. Its dense crosslinked microstructure provides excellent barrier properties, wear resistance, chemical resistance, and UV resistance, effectively protecting metal structures from moisture and corrosion.
With high solid content, it allows for low or zero VOC emissions and achieves the required film thickness in a single application, enhancing efficiency and reducing costs. Ideal as a topcoat for heavy-duty anti-corrosion coatings, it offers exceptional durability and long-lasting UV resistance (QUV 4000 hours), making it suitable for engineering vehicles, wind power, water parks, and offshore platforms.
| Item | Result |
|---|---|
| Adhesion | Grade 1 |
| Impact Strength | ≥50kg.cm |
| Hardness | 2 - 3H |
| Flexibility | ≤1mm |
| Abrasion Resistance | ≤0.03g |
| Acid Resistance (240h in 5% Sulfuric Acid Solution) | No corrosion, no blistering, no detachment |
| Alkaline Resistance (240h in 5% Sodium Hydroxide Solution) | No corrosion, no blistering, no detachment |
| Salt Resistance (240h in 5% Sodium Chloride Solution) | No corrosion, no blistering, no detachment |
| Oil Resistance (240h) | No corrosion, no blistering, no detachment |
| Water Resistance (30d) | No corrosion, no blistering, no detachment |
| Salt Fog Resistance | 2000h |
| UV Resistance | 4000h |
| Thermal - Cycle Test (3 cycles) | Paint film intact, no abnormalities |
| Water Vapor Permeability | 0.007 |
| Chloride Ion Permeability | 0.7×10⁻⁴ |
Polyaspartic Polyurea Floor Coatings
| Item | Result |
|---|---|
| Adhesion Strength | ≥4.0MPa |
| Tensile Strength | ≥16MPa |
| Elongation at Break | 300 - 400 |
| Tear Strength | ≥70KN/M |
| Hardness (Shore A) | ≥80 |
| Low - temperature Flexibility | -40°C |
| Abrasion Resistance (750/500r) | ≤0.03g |
| Acid Resistance (240h in 5% Sulfuric Acid) | No corrosion, no blistering, no detachment |
| Alkaline Resistance (240h in 5% Sodium Hydroxide) | No corrosion, no blistering, no detachment |
| Salt Resistance (240h in 3% Sodium Chloride) | No corrosion, no blistering, no detachment |
| Oil Resistance (240h) | No corrosion, no blistering, no detachment |
| Water Resistance (30d) | No corrosion, no blistering, no detachment |
Polyaspartic Polyurea Flooring Topcoat
Performance Features: Excellent UV resistance, good color retention, high hardness with toughness, strong impact and abrasion resistance, and excellent adhesion to various substrates. Suitable for weather-resistant topcoats on wind turbine blades and flooring applications.
| Item | Result |
|---|---|
| Adhesion | ≥10.0MPa |
| Tensile Strength | ≥16MPa |
| Elongation at Break | ≥50 |
| Tear Strength | ≥70KN/M |
| Flexibility | ≤1mm |
| Low - temperature Flexure | -40°C |
| Abrasion Resistance (750/500r) | ≤0.03g |
| Acid Resistance (240h in 5% Sulfuric Acid) | No corrosion, no blistering, no detachment |
| Alkaline Resistance (240h in 5% Sodium Hydroxide) | No corrosion, no blistering, no detachment |
| Salt Resistance (240h in 3% Sodium Chloride) | No corrosion, no blistering, no detachment |
| Oil Resistance (240h) | No corrosion, no blistering, no detachment |
| Water Resistance (30d) | No corrosion, no blistering, no detachment |
Polyaspartic Polyurea Potting Glue And Crystal Glue
Polyaspartic Polyurea Battery and Circuit Potting Adhesive
Due to its excellent weather resistance, polyaspartic polyurea is widely used for power battery encapsulation and potting. It also features flame retardancy, which helps delay the aging and flammability of battery potting materials, reducing the risk of thermal runaway and ensuring driver safety.
Polyaspartic Polyurea Crystal Clear Resin That Never Yellows
Due to the larger molecular spatial steric hindrance and UV resistance properties of Polyaspartic Polyurea, crystal products made from Polyaspartic Polyurea, compared to traditional epoxy resins, have the advantages of being non-yellowing and having high transparency. Additionally, they are easier to manufacture and less prone to breaking compared to crystals.
PACKING
PACKING
200 Kgs/Drum, 20 Kgs/Drum
SHELF LIFE
1520 must be stored in airtight containers to prevent contact with moisture. Recommended storage temperature is below 40°C (≤104°F). The shelf life of 1520 in the original closed container is 12 months.
NOTICE
1520 is combustible and should be stored below 40 ℃. It should be kept away from fire source and stored in a cool, dry, and ventilated environment. The storage period is 12 months.
he coating formulated with 1520 should be tested for performance after one week’s maintenance.
Note: This manual is for reference only, without any warranty. In view of the limitation of resin function and the diversity of user requirements, please strictly test the adaptability of the product and the stability of the final product. The technical information is subject to change without prior notice.